AVTOZYATLARI/KAMCHILIKLARISANOATLARILOVALARMESHLASHPAYVANDARISHIssiqlik bilan ishlov berish
Afzalliklar / Kamchiliklar
3004 alyuminiy - mukammal korroziyaga chidamliligi bilan umumiy maqsadli qotishma. Uning tarkibi 3003 alyuminiy qatlamga o'xshaydi, ammo magniyning ozgina qo'shilishi uning kuchini oshiradi. Ushbu sinfning kamchiliklaridan biri shundaki, uni issiqlik bilan ishlov berish mumkin emas.
KIMYOVIY XUSUSIYATLARI
| Kun.k. | Si | Fe | MN | MG | ZN |
|---|---|---|---|---|---|
| 0.25 foiz | 0.30 foiz | 0.70 foiz maksimal | 1-1.50 foiz | 0.80-1.30 foiz | 0.25 foiz |
MEXANIK XUSUSIYATLARI
| BAJA | KUCH (METRIK/IMPERIAL) | UZAYISH | QATTIQLIK | |||
|---|---|---|---|---|---|---|
| Jahl | Eng yuqori kuchlanish kuchi | Yakuniy hosil kuchi | Kesish kuchi | Charchoq kuchi | foiz | Brinell |
| 3004-O | 180 MPa / 26,000 psi | 69 MPa / 10, 000 psi | 110 MPa / 16,000 psi | 97 MPa / 14, 000 psi | 20-25 | 45 |
| 3004-H34 | 215 MPa / 31,000 psi | 170 MPa / 25,000 psi | 115 MPa / 17, 000 psi | 105 MPa / 15, 000 psi | 10-17 | 52 |
| 3004-H36 | 240 MPa / 35, 000 psi | 200 MPa / 25,000 psi | 125 MPa / 18, 000 psi | 105 MPa / 15,000psi | 9-12 | 63 |
| 3004-H36 | 260 MPa / 38,000 psi | 230 MPa / 33, 000 psi | 140 MPa / 20, 000 psi | 110 MPa / 16,000 psi | 5-9 | 70 |
| 3004-H38 | 285 MPa / 41,000 psi | 250 MPa / 36,000 psi | 145 MPa / 21,000 psi | 110 MPa / 16,000 psi | 4-6 | 77 |
TEZ-TEZ SO'RALADIGAN SAVOLLAR
3003 VA 3004 ALyuminiy O'RASINDAGI FARQ QANDAY?3004 ALyuminiydan ISHLASH UCHUN ISHLATILADIMI?3004 QANDAY FOYDALANIShLAR?
3003 va 3004 alyuminiy o'rtasidagi farq nima?
JAVOB:
Ushbu ikkita umumiy maqsadli qotishmalar juda o'xshash. Kimyoviy tarkibi bo'yicha 3004 alyuminiy tarkibida magniy qo'shilishi mavjud bo'lib, u kuchlilik jihatidan ushbu sinfga ustunlik beradi.