TIPIAL STANDARTLAR
| BAJA | O'lchamlar muntazam ravishda saqlanmoqda | ||
|---|---|---|---|
| Jahl | Qalinligi (Metrik/Imperial) | Kengligi | Uzunlik |
| 3003-O | .25 - 6mm / 1/64- 15/64" | 36", 48", 60" | 96", 120", 144" |
| 3003-H12 | .25 - 6mm / 1/64- 15/64" | 36", 48", 60" | 96", 120", 144" |
| 3003-H14 | .25 - 6mm / 1/64- 15/64" | 36", 48", 60" | 96", 120", 144" |
| 3003-H16 | .25 - 6mm / 1/64- 15/64" | 36", 48", 60" | 96", 120", 144" |
| 3003-H18 | .25 - 6mm / 1/64- 15/64" | 36", 48", 60" | 96", 120", 144" |
3003 ALyuminiy lavha HAQIDA BATAFSIL MA'LUMOT
AVTOZYATLARI/KAMCHILIKLARISANOATLARILOVALARMESHLASHPAYVANDARISHIssiqlik bilan ishlov berish
Afzalliklar / Kamchiliklar
U yuqori kuchlanish va yaxshi korroziyaga chidamliligiga ega. Boshqa tomondan, alyuminiy issiqlik bilan ishlov berishga javob bermaydi.
KIMYOVIY XUSUSIYATLARI
| MG | CR | Kun.k. | Fe | ZN |
|---|---|---|---|---|
| 0.60 foiz | 0.70 foiz | 0.20 foiz | 1 -1.50 foiz | 0.10 foiz |
MEXANIK XUSUSIYATLARI
| BAJA | KUCH (METRIK/IMPERIAL) | UZAYISH | QATTIQLIK | ||
|---|---|---|---|---|---|
| Jahl | Maksimal kuchlanish kuchi (Min - Maks) | Daromad to'plami 0,2 foiz | foiz 1/16" | 1/2" | Brinell |
| 3003-0 | 97 - 131 MPa / 14,000 - 19,000 psi | 41 MPa % 2f 6000 psi | 30 foiz | 40 | 28 |
| 3003-H12 | 117 -158 MPa / 17,000 - 23,000 psi | 124 MPa / 18, 000 psi | 10 foiz | 20 | 35 |
| 3003-H14 | 137 - 179 MPa / 20,000 - 26,000 psi | 141 MPa / 21, 000 psi | 8 foiz | 16 | 40 |
| 3003-H16 | % 7b{0}} MPa / 24,000 - 30,000 psi | 172 MPa / 25, 000 psi | 5 foiz | 15 | 47 |
| 3003-H18 | 186 - 227 MPa / 27,000 - 33,000 psi | 186 MPa / 27, 000 psi | 4 foiz | 10 | 55 |
TEZ-TEZ SO'RALADIGAN SAVOLLAR
3003 VA 3004 ALyuminiy O'RASINDAGI FARQ QANDAY?3003 ALyuminiydan AVTO SAVOLIDA ISHLATILADIMI?3003 ALyuminiy Oson payvandlanadimi?
3003 va 3004 alyuminiy o'rtasidagi farq nima?
JAVOB:
3003 alyuminiy umumiy maqsadli qotishma bo'lib, o'rtacha quvvat, yaxshi shakllanuvchanlik, ishlov berish qobiliyatini namoyish etadi va osongina chiziladi. U 1100 alyuminiydan taxminan 20 foizga ko'proq kuchni ko'rsatadi va uning asosiy qotishma elementi marganetsdir. U kundalik mahsulotlarda apparat va anjomlardan tortib, metall plitalar ishlab chiqarish va avtomobil qismlariga qadar namoyon bo'ladi. U 3004 ga juda o'xshash deb hisoblanadi. Ikki alyuminiy sinf o'rtasidagi asosiy farq bu kuchdir. 3003 alyuminiydan farqli o'laroq, 3004 tarkibida 1 foiz magniy qo'shiladi, bu unga ko'proq kuch beradi va 5052 alyuminiy darajasiga yaqinlashadi.